文献索引:10.1016/j.intermet.2018.01.013
全文:HTML全文
The long-term creep behaviour of the cast Ti-44.4Al-8.1Ta (at.%) alloy with an initial γ-TiAl(L10)+α2-Ti3Al(D019) microstructure was investigated at 700 °C. The alloy shows a remarkable creep resistance. The minimum creep rate is measured to be as low as 1.47 × 10−10 s−1 and total deformation is only 2.5% after an interrupted 30000 h creep test at 200 MPa. The creep exposure affects the stability of the initial microstructure. The discontinuous precipitation leads to the formation of γ + τ(Ti3Al2Ta) type of microstructure along the lamellar colony and grain boundaries. The decomposition of the α2 phase results in the formation of τ and γ + α2 + L12 segments within the lamellae and cellular γ + α2 + L12 network within the coarse particles. The intensive formation and coalescence of the cavities along the grain boundaries leads to predominantly intergranual type of creep fracture at the applied stresses of 250 and 300 MPa.
|
Influence of unique layered microstructure on fatigue proper...
2018-02-03 [10.1016/j.intermet.2018.01.009] |
|
Application of laser remelting process on the Zr-Cu based al...
2018-02-03 [10.1016/j.intermet.2018.01.012] |
|
Ferromagnetic ordering in the novel ternary uranium germanid...
2018-02-03 [10.1016/j.intermet.2018.01.011] |
|
Effect of solution and aging treatment on the microstructure...
2018-02-03 [10.1016/j.intermet.2018.01.007] |
|
Precipitation behavior and mechanical properties of Ti-Ni-Nb...
2018-02-03 [10.1016/j.intermet.2018.01.014] |
首页 |
期刊大全 |
MSDS查询 |
化工产品分类 |
生物活性化合物 |
关于我们 |
免责声明:知识产权问题请联系 service1@chemsrc.com
Copyright © 2024 ChemSrc All Rights Reserved