The near-infrared broadband emission from bismuth-doped GeO2-WO3 and GeO2-BaO glasses.
Haiping Xia, Xuejun Wang
Index: Spectrochim. Acta. A. Mol. Biomol. Spectrosc. 70(1) , 122-5, (2008)
Full Text: HTML
Abstract
Glasses with the composition of (99.5-chi)GeO2-chiWO(3)-0.5Bi2O3 (chi=3, 6, 9 mol%) and (99.5-psi)GeO2-psiBaO-0.5Bi2O3 (psi=3, 6, 9 mol%) were prepared. Their thermal, emission and absorption measurements were carried out. The near-infrared super broadband emission of the prepared samples peak around 1.3 microm was discovered. The results indicated, in GeO2-WO3-Bi2O3 glasses, increasing amount of WO3 brought about the broadening of FWHM, prolonging of lifetime and enhancing of thermal stabilities. While in GeO2-BaO-Bi2O3 glasses, concomitant with the increasing amount of BaO were the broadened FWHM as well as the prolonged lifetime. Red-shift tendency of absorption edges was discovered in both two groups of glasses indicating the Bi5+ ions might take responsibility for the broadband emission.
Related Compounds
Related Articles:
2007-03-01
[J. Nanosci. Nanotechnol. 7(3) , 1006-13, (2007)]
2009-01-01
[Dent. Mater. 25(11) , 1411-8, (2009)]
Enhancement of ferroelectric polarization stability by interface engineering.
2012-03-02
[Adv. Mater. 24(9) , 1209-16, (2012)]
Oxygen-17 hyperfine structures in the pure rotational spectra of SrO, SnO, BaO, HfO and ThO.
2007-11-28
[Phys. Chem. Chem. Phys. 9(44) , 5897-901, (2007)]
2011-09-01
[Spectrochim. Acta. A. Mol. Biomol. Spectrosc. 79(5) , 1251-5, (2011)]